SETAL A U 601 HV TBA is in the formulation of fast-drying hard-wearing wood finishes and DIY and decorative sealers. General SETAL A U 601 HV TBA is an isocyanate-modified alkyd resin with a high crosslinking density. The paint films are characterised by their good performance properties such as hardness and flexibility. They are therefore highly resistant to wear and abrasion. They also have good resistance towater and household cleaning agents. The use of the following driers is recommended: 0.03 % cobalt 6, 0.60 % zirconium 18 and 0.10 % calcium 4. The metal content is always calculated on the solvent-free resin.Methylethyl ketoximen has proved ideal as an anti-skinning agent for these formulations. The amount required is 1.0 %, calculated on the solvent-free binder. Wood finishes: typical applications for SETAL A U 601 HV TBA include the formulation of coatings for indoor use, e.g. for doors and window frames and for parquet flooring. It can also be used in coatings for garden furniture, boats and other such substrates. Coatings based on SETAL A U 601 HV TBA can be matted easily with small amounts of matting agent. Combination of SETAL A U 601 HV TBA with SETAL A F 681 yields highbodied gloss coatings. The brushability, especially of DIY paints, can be optimised by the addition of small amounts of SETAL A U 601 TIX TBA (approx. 5 - 10%, calculated on SETAL A U 601 HV TBA). Coatings based on SETAL A U 601 HV TBA dry to formdefectfree films on most tropical woods so no special impregnation is necessary beforehand. However, given the many different types of tropical woods and their very different properties and constituents, trials should always be carried out. Important - Depending on their viscosity, coatings based on SETAL A U 601 HV TBA can be applied by brushing, rolling or spraying. Sprayingmust be carried out inwaterrinsed spray booths. Spray mists must be regularly removed to prevent ignition.

Air and forced drying industrial coatings with fast drying and high hardness. Specialty coatings for glass, precious metals and plastics. It is used as air drying coating systems Viacryl SC 200/40X is mainly used for fast drying industrial paints. The dried films are noted for very high hardness and excellent resistance poperties e.g. against water and diluted acids. For air-dried systems (tack-free in 15 minutes) Viacryl SC 200 can be used alone or in combination with plasticizers. Such systems compared with systems using Viacryl SC 200 as sole binder show better pigment wetting and flexibility. The use of plasticizers will, however have a negative influence on alkali resistance. The compatibility of Viacryl SC 200 with other coatings ingredients should be controlled from time to time. Stoving enamels For stoving systems Viacryl SC 200 is generally formulated with plasticizers and urea or melamine resins. The following ratios habe proven successful: Viacryl SC 200 : amino resin : plasticizer = 70 : 15 : 15 or 65 : 15 : 20 (on solids). Compared with air drying systems such systems show after curing (e. g. 30 min/140 °C) improved flexibility, hardness, impact and chip resistance. Specialty coatings For air drying as well as stoving systems Viacryl SC 200 can be used to formulate specialty coatings with good adhesion to glass, precious metals, and various plastics such as ABS and polyphenylene oxide (PPO).

SETALUX 2117 XS-30 is a fast drying component. It si used as fast drying clearcoat for car repair.

VIACRYL SC 121/60X is a sole binder for road-marking paints. Fast drying primers and top coats for nonferrous metal and plastic substrates.It is used as road-marking paints Viacryl SC 121/60LG was especially developed as sole binder for road-marking paints. Road-marking paints based on this copolymer have excellent adhesion and abrasion resistance, permanent flexibility as well as good whiteness retention. It is, however, recommended to first conduct a trial application under the given conditions to ensure suitability. Coating of plastics One-coat paints based on Viacryl SC 121 show especially good adhesion to plastics such as PVC, acrylic sheet, polycarbonate and polyester reinforced components.Primers and top-coats on metallic substrates. In view of its fast initial and through drying as well as its good water resistance Viacryl SC 121 is suitable for formulation one-coat paints and industrial primers. Coatings based on this product show good adhesion to steel, aluminium and zinc. For aluminium substrates a binder pigment ratio of about 1 : 2 should be selected. For steel a ratio of 1 : 1.5 is recommended. Decorative finishes are generally pigmented in ratios of 1 : 1 (binder/pigment) on solids.