SETAL A F 681 TBA is in the formulation of decorative paints with excellent through-drying and good yellowing resistance. Also for flow coatings, DIY paints and air-drying coatings. General SETAL A F 681 TBA is low-viscosity long-oil alkyd resin which is ideal for use in the formulation of DIY and decorative paints with excellent through-drying, a dust-free drying time of approx. 3.5 hours and a tack-free drying time of approx. 6 hours. Because of the relatively high acid value of SETAL A F 681 TBA, the following driers should be used: 0.04 % colbalt 6, 1.20 % zirconium 18 and 0.20 % calcium 4. The metal content is always calculated on the solvent-free resin. The use of these driers ensures good drying stability, even after prolonged storage. The addition of an anti-skinning agent is recommended. Aliphatic hydrocarbons are used to thin SETAL A F 681 TBA. Higher boiling fractions are particularly suitable for adjusting the brushing viscosity. Standard pigments can be used to colour the formulations. The compatibility with alkaline pigments must always be tested in each individual case

SETAL A E 41 X is a short-oil, fatty acid-modified alkyd resin with extremely low viscosity. In the formulation of nitrocellulose lacquers for wood. Nitrocellulose lacquers. SETAL A E 41 X is an alkyd resin with extremely low viscosity for use in the formulation of nitrocellulose lacquers. It is characterized in particular by the following: unusually fast drying rates, especially at high wet film thicknesses, high flexibility and hardness, excellent sandability and high body combined with good sag resistance of the films on wood, excellent lightfastness, excellent intercoat adhesion. The extremely low viscosity of SETAL A E 41 X results in higher solids contents. SETAL A E 41 X can be combined in various ratios with nitrocellulose to formulate wood lacquers. Because of its unusually fast drying rates, SETAAL A E 41 X has gained particular significance in wood lacquers for application on production lines using conveyor dryers.

SETAL 84 XX-70 is a very good durability, excellent colour and gloss retention , high body. It is used: Stoving enamels, car body enamels, enamels for domestic appliances, laboratory equipment, electric apparatus etc. Clear and pigmented acid curing finishes. Clear and pigmented nitrocellulose lacquers. Clear and pigmented polyurethane lacquers. Roller coatings for high stoving temperatures (120-160 °C), especially overprint varnishes. Coil coatings.

SETAL A U 601 HV TBA is in the formulation of fast-drying hard-wearing wood finishes and DIY and decorative sealers. General SETAL A U 601 HV TBA is an isocyanate-modified alkyd resin with a high crosslinking density. The paint films are characterised by their good performance properties such as hardness and flexibility. They are therefore highly resistant to wear and abrasion. They also have good resistance towater and household cleaning agents. The use of the following driers is recommended: 0.03 % cobalt 6, 0.60 % zirconium 18 and 0.10 % calcium 4. The metal content is always calculated on the solvent-free resin.Methylethyl ketoximen has proved ideal as an anti-skinning agent for these formulations. The amount required is 1.0 %, calculated on the solvent-free binder. Wood finishes: typical applications for SETAL A U 601 HV TBA include the formulation of coatings for indoor use, e.g. for doors and window frames and for parquet flooring. It can also be used in coatings for garden furniture, boats and other such substrates. Coatings based on SETAL A U 601 HV TBA can be matted easily with small amounts of matting agent. Combination of SETAL A U 601 HV TBA with SETAL A F 681 yields highbodied gloss coatings. The brushability, especially of DIY paints, can be optimised by the addition of small amounts of SETAL A U 601 TIX TBA (approx. 5 - 10%, calculated on SETAL A U 601 HV TBA). Coatings based on SETAL A U 601 HV TBA dry to formdefectfree films on most tropical woods so no special impregnation is necessary beforehand. However, given the many different types of tropical woods and their very different properties and constituents, trials should always be carried out. Important - Depending on their viscosity, coatings based on SETAL A U 601 HV TBA can be applied by brushing, rolling or spraying. Sprayingmust be carried out inwaterrinsed spray booths. Spray mists must be regularly removed to prevent ignition.