ADDITOL XL 102 is used to improve the effectiveness of paint removers containing paraffine and wax. Post treatment with organic solvents is not necessary.

ADDITOL VXL 4930 may be used in all solvent-containing and water-dilutable paint systems. It promotes the spray dust absorption, prevents orange peel and increases scratch resistance. ADDITOL VXL 4930 is effective at low concentrations and at the correct dosage, does not adversely affect intercoat adhesion. Blistering, cratering and floating in pigment blends are effectively prevented. It does not stabilize the foam during paint production and application. The substrate wetting is advanced.ADDITOL VXL 4930 is used primarily in industrial stoving/baking paints and 2K PUR paint systems.

ADDITOL VXW 6386 Easy emulsifable defoamer, espacially for high quality waterborne sytems, at there conventionally mineral-oil or silicon based defoamers cause decrease the surface quallity of the film (orange peel, craters). At forced and stoving drying paints it can observed a higher cissing free filmthickness. ADDITOL VXW 6386 is qualified for following waterborne systems: stoving enamel based on alkyd- or acrylic-melamine resin, 2 component acrylic-isocyanate paints, paints based on waterdilutable alkyd resin and gloss and semigloss dispersion paint.

ADDITOL XL 6568 is used for the formulation of stripping enamels, release agents and temporary corrosion protection. ADDITOL XL 6568 is added to stripping enamels as anti adhesion promotor. Coatings of this nature give temporary protection against mechanical attack and corrosion to various substrates. Such coatings can easily be pealed off later. ADDITOL XL 6568 can be used in solvent based as well as in aqueous systems. Suitable binders for solvent based systems are the Hostaflex grades CM 150 and CM 133 as well as the Mowital grades B30HH and B60H. To formulate aqueous systems, acrylic dispersions like Ucecryl B 3022 are recommended. While solvent based release coatings can easily be removed from metallic substrates aqueous systems based on styrene acrylate dispersions can also be removed from glass, pottery, wood and plastics. For formulating systems with high film strength aqueous systems are more suitable than solvent based systems.