Paints & Coatings

ADDITOL XL 6507 product, serving for trial purposes only. Deviations which might occur during transfer into manufacturing in a commercial scale are possible and do not constitute any material defect. ADDITOL XL 6507 is a solution of defoaming polymers without siliconeSuggested applications are - industrial coatings - 2 comp. acrylic/isocyanate systems - corrosion protection paints based on epoxy resins - wood and furniture coatings based on unsaturated polyesters and UV-curing systems In non-pigmented systems over dark surfaces, a slight turbidity, depending on the added amount, may occur.

ADDITOL XL 122 N is a paint additive to enhance mar resistance and slip and to improve flow and levelling in air drying and stoving paints. ADDITOL XL 122 N is a silicone type paint additive. It enhances the resistance of solventborne paints to mechanical attack by increasing the slip of the paint surface. Furthermore, ADDITOL XL 122 N improves levelling and flow prevents surface defects like orange peel and thus in general contributes to the formation of flawless film surfaces with enhanced sheen. In coil coating and can coating paints as well as in furniture enamels ADDITOL XL 122 N is used to prevent blocking also. ADDITOL XL 122 N can be employed with air drying alkyd resin paints, alkyd resin stoving paints, thermosetting acrylic paints, nitrocellulose lacquers, acid curing paints, alkyd-isocyanate paints or acrylics, isocyanate enamels. Paints containing ADDITOL XL 122N can be recoated in general without additional treatment of the surface. The effect of ADDITOL XL 122N varies with the formulation of the paint. A level of 0.05 to 0.3 % of ADDITOL XL 122N on the finished paint may serve as a guide.

High pigment loading without increase in viscosity. Reduction of dispersing time. Enhances gloss and levelling. For air drying and stoving solvent-borne paints and particularly for water dilutable paint systems. ADDITOL XL 203 prevents the floating of titanium dioxide in conjunction with organic or inorganic coloured pigments. It can be employed in solvent-borne and water dilutable air drying and stoving paint systems. ADDITOL XL 203 enhances gloss and levelling of paint films. Pigment loading of paints and pigment pastes can be increased without rises in viscosity. Dispersion time is reduced. The recommended level may range from 0.1 to 1.5 % on total paint. Level on pigments: inorganic pigments: 0.5 - 2.5 %, organic pigments: 1.5 - 5 %. The figures given here may serve as a guide for extensive trials to find the optimum in dosage and effect and to save costs. Since ADDITOL XL 203 is a cationic product it should not be used in conjunction with certain anionic products. Phase seperation occurs and ADDITOL XL 203 becomes ineffective at once. The compatibility should be determined by experiments. ADDITOL XL 203 can be combined with cationic and non-ionic products.

ADDITOL XL 203 is a high pigment loading without increase in viscosity. Reduction of dispersing time. For air drying and stoving solvent-borne paints and for water dilutable paint systems. ADDITOL XL 204 prevents the floating of titanium dioxide in conjunction with organic or inorganic coloured pigments. It can be employed in solvent-borne and water dilutable air drying and stoving paint systems. ADDITOL XL 204 affords higher pigment loading of the paint system and pigment pastes without causing the viscosity rise usual with such products and, at the same time, reduces dispersing time. The recommended level may range from 0.1 to 1.5 % on total paint. Level on pigments: inorganic pigments: 0.5 - 2.5 % organic pigments: 1.5 - 5.0 %, Levels of addition in water dilutable air drying and stoving system may range from 1 to 6 % on pigments. The figures given here may serve as a guide for extensive trials to find the optimum in dosage and effect to save costs.