SETAL A F 681 TBA is in the formulation of decorative paints with excellent through-drying and good yellowing resistance. Also for flow coatings, DIY paints and air-drying coatings. General SETAL A F 681 TBA is low-viscosity long-oil alkyd resin which is ideal for use in the formulation of DIY and decorative paints with excellent through-drying, a dust-free drying time of approx. 3.5 hours and a tack-free drying time of approx. 6 hours. Because of the relatively high acid value of SETAL A F 681 TBA, the following driers should be used: 0.04 % colbalt 6, 1.20 % zirconium 18 and 0.20 % calcium 4. The metal content is always calculated on the solvent-free resin. The use of these driers ensures good drying stability, even after prolonged storage. The addition of an anti-skinning agent is recommended. Aliphatic hydrocarbons are used to thin SETAL A F 681 TBA. Higher boiling fractions are particularly suitable for adjusting the brushing viscosity. Standard pigments can be used to colour the formulations. The compatibility with alkaline pigments must always be tested in each individual case

VIACRYL SC 341/60SNABAC has a superior radiance, high surface hardness, excellent weather resistance. Medium solid acrylic resin for uni-coloured automobile finishes and isocyanate systems. With light stabilizers for clear coats over metallic basecoats. Easy and safe application. Viacryl SC 341 is used in combination with amino resins, preferably with reactive melamine resins. Polyurethane based thickness layer coatings can be formulated in combination with aliphatic polyisocyanates (e.g. Desmodur N). Stoving paints Suitable crosslinkers for Viacryl SC 341 in the first place are butylated melamine resins in a resin solids ratio of from 70 : 30 to 80 : 20. Spray application of paints on Viacryl SC 341 is excellent. Even when applied in thick layer, there is only a slight tendency to saging on vertical surfaces and to blistering or popping during stoving. The paints may also be rendered thicotropic with silicates, without the gloss being reduced. Film properties. Film of paints on Viacryl SC 341 have a superior decorative performance, like radiant brilliance, excellent levelling and very good build besides great hardness and gasoline resistance. Weathering tests in Florida showed very finishes.

VIALKYD AV 608/60WS is easy to use, excellent weather resistance, good water and corrosion resistance, high gloss. Sole binder for aluminium paints with brilliant effect and good gloss retention. Used for zinc dust paints, mica iron paints, and anticorrosive paints. VIALKYD AV 608 is a styrene-modified oil which is characterized by high resistance to water and corrosion. In aluminium-pigmented paints it yields a brilliant effect, good gloss retention and excellent weather resistance. It is used as sole binder for high-build, readily brushable, air drying aluminium, zinc dust and mica iron paints, zinc chromate primers, and lead and chromate-free ground coats. On account of its high degree of water resistance it is used for paint coating of steel structures such as oil and gas tanks, hall and brigde constructions, etc. VIALKYD AV 608/60WS may show some cloudiness, which, however, does not influence the technical properties of the paint.

SETALUX 1196 VV-60YA is in combination with aliphatic poly-isocyanates: fast drying, good through harden-ing, good chemical resistance, good light fastness, good compatibility with poly isocyanates. It is used as industrial lacquers with good adhesion on difficult substrates. Lacquers with good adhesion on a number of plastic substrates.