Sơn & Sơn phủ

SETAL 1201 SM-50 is Good hardness, fast drying and abrasion resistant. It is used as decorative varnishes.

SETAL A F 48 TB/X is in the formulation of high-quality, air and force-drying industrial coatings, radiator paints, special effect finishes, primers and DIY paints. SETAL A F 48 TB/X is the standard binder for air and force-drying industrial coatings. Itsmain characteristics are its rapid drying (four-hour coating), good through-drying and curing to formdefect-free films, even in thick coats. It also yields good film properties - whiteness, resistance to yellowing, gloss and gloss retention, brilliance, body, flow and weather stability. SETAL A F 48 TB/X can be used in primers as well as in all types of top coats and one-coat finishes. Coatings based on SETAL A F 48 TB/X can be applied using conventional methods such as spraying, dipping and flow coating. A combination of 0.1 % Ca/0.06 % Co/0.2 % Zn and 0.2 % Zr-octoate, calculated as metal on solvent-free resin, has proved to be a useful mixture for speeding up the drying. Combination with long-oil alkyd resins is necessary for DIY paints applied by brushing.

ROSKYDAL XP 2072 is especially suitable for conventional- or UV-curing (transparent or pigmented) topcoats and pigmented sealers for wood and furniture. properties for applications by spraying or curtain in UV- or conventionalcuringsystems. ROSKYDAL XP 2072 is usually used as the sole binder. If made necessary by the application (high amount) and compatibility exists, it can be flexibilized with other ROSKYDAL grades, e.g. ROSKYDAL 550 or E 70.

SETAL A U 601 HV TBA is in the formulation of fast-drying hard-wearing wood finishes and DIY and decorative sealers. General SETAL A U 601 HV TBA is an isocyanate-modified alkyd resin with a high crosslinking density. The paint films are characterised by their good performance properties such as hardness and flexibility. They are therefore highly resistant to wear and abrasion. They also have good resistance towater and household cleaning agents. The use of the following driers is recommended: 0.03 % cobalt 6, 0.60 % zirconium 18 and 0.10 % calcium 4. The metal content is always calculated on the solvent-free resin.Methylethyl ketoximen has proved ideal as an anti-skinning agent for these formulations. The amount required is 1.0 %, calculated on the solvent-free binder. Wood finishes: typical applications for SETAL A U 601 HV TBA include the formulation of coatings for indoor use, e.g. for doors and window frames and for parquet flooring. It can also be used in coatings for garden furniture, boats and other such substrates. Coatings based on SETAL A U 601 HV TBA can be matted easily with small amounts of matting agent. Combination of SETAL A U 601 HV TBA with SETAL A F 681 yields highbodied gloss coatings. The brushability, especially of DIY paints, can be optimised by the addition of small amounts of SETAL A U 601 TIX TBA (approx. 5 - 10%, calculated on SETAL A U 601 HV TBA). Coatings based on SETAL A U 601 HV TBA dry to formdefectfree films on most tropical woods so no special impregnation is necessary beforehand. However, given the many different types of tropical woods and their very different properties and constituents, trials should always be carried out. Important - Depending on their viscosity, coatings based on SETAL A U 601 HV TBA can be applied by brushing, rolling or spraying. Sprayingmust be carried out inwaterrinsed spray booths. Spray mists must be regularly removed to prevent ignition.