เคมีภัณฑ์ชนิดพิเศษ

SETAL A F 26 X is in the formulation of primers, knifing fillers, primer surfacers, top coats and dipping paints and flow coatings for radiators. Coatings based on SETAL A F 26 X are characterised by their very rapid drying and curing, high resistance to yellowing, weather stability and good anticorrosion properties. The use of alkaline pigments such as zinc phosphate, zinc oxide and aluminium triphosphate make it possible to optimize the anticorrosion properties of primers based on SETAL A F 26 X. Knifing fillers and primer surfacers applied in thickness of up to 200 μm can be dry-sanded within 1 hour. Combination with aminoplastic resins is recommended when formulating force-drying coatings.

SETAL AF 681 TB is in the formulation of decorative paints with excellent through-drying and good yellowing resistance. Also for flow coatings, DIY paints and air-drying coatings. General Setal A F 681 TB is a low-viscosity long-oil alkyd resin which is ideal for use in the formulation of DIY and decorative paints with excellent through-drying, a dust-free drying time of approx. 3.5 hours and a tack-free drying time of approx. 6 hours. Because of the relatively high acid value of Setal A F 681 TB, the following driers should be used: 0.04 % cobalt 6, 1.20 % zirconium 18 and 0.20 % calcium 4. The metal content is always calculated on the solvent-free resin. The use of these driers ensures good drying stability, even after prolonged storage. The addition of an anti-skinning agent is recommended. Aliphatic hydrocarbons are used to thin Setal A F 681 TBA. Higher boiling fractions are particularly suitable for adjusting the brushing viscosity. Standard pigments can be used to colour the formulations. The compatibility with alkaline pigments must always be tested in each individual case.

Air and forced drying industrial coatings with fast drying and high hardness. Specialty coatings for glass, precious metals and plastics. It is used as air drying coating systems Viacryl SC 200/40X is mainly used for fast drying industrial paints. The dried films are noted for very high hardness and excellent resistance poperties e.g. against water and diluted acids. For air-dried systems (tack-free in 15 minutes) Viacryl SC 200 can be used alone or in combination with plasticizers. Such systems compared with systems using Viacryl SC 200 as sole binder show better pigment wetting and flexibility. The use of plasticizers will, however have a negative influence on alkali resistance. The compatibility of Viacryl SC 200 with other coatings ingredients should be controlled from time to time. Stoving enamels For stoving systems Viacryl SC 200 is generally formulated with plasticizers and urea or melamine resins. The following ratios habe proven successful: Viacryl SC 200 : amino resin : plasticizer = 70 : 15 : 15 or 65 : 15 : 20 (on solids). Compared with air drying systems such systems show after curing (e. g. 30 min/140 °C) improved flexibility, hardness, impact and chip resistance. Specialty coatings For air drying as well as stoving systems Viacryl SC 200 can be used to formulate specialty coatings with good adhesion to glass, precious metals, and various plastics such as ABS and polyphenylene oxide (PPO).

SETALUX 1903 BA-75 provides VOC compliant coatings (420 g/l) with high build and gloss, good mechanical properties, good chemical resistance and good outdoor durability (in combination with aliphatic poly-isocyanates). It is used as two-component clearcoats and solid colours for vehicle refinish. Two-component industrial topcoats.