SETAL A F 681 TBA is in the formulation of decorative paints with excellent through-drying and good yellowing resistance. Also for flow coatings, DIY paints and air-drying coatings. General SETAL A F 681 TBA is low-viscosity long-oil alkyd resin which is ideal for use in the formulation of DIY and decorative paints with excellent through-drying, a dust-free drying time of approx. 3.5 hours and a tack-free drying time of approx. 6 hours. Because of the relatively high acid value of SETAL A F 681 TBA, the following driers should be used: 0.04 % colbalt 6, 1.20 % zirconium 18 and 0.20 % calcium 4. The metal content is always calculated on the solvent-free resin. The use of these driers ensures good drying stability, even after prolonged storage. The addition of an anti-skinning agent is recommended. Aliphatic hydrocarbons are used to thin SETAL A F 681 TBA. Higher boiling fractions are particularly suitable for adjusting the brushing viscosity. Standard pigments can be used to colour the formulations. The compatibility with alkaline pigments must always be tested in each individual case

SETAL A E 41 X is a short-oil, fatty acid-modified alkyd resin with extremely low viscosity. In the formulation of nitrocellulose lacquers for wood. Nitrocellulose lacquers. SETAL A E 41 X is an alkyd resin with extremely low viscosity for use in the formulation of nitrocellulose lacquers. It is characterized in particular by the following: unusually fast drying rates, especially at high wet film thicknesses, high flexibility and hardness, excellent sandability and high body combined with good sag resistance of the films on wood, excellent lightfastness, excellent intercoat adhesion. The extremely low viscosity of SETAL A E 41 X results in higher solids contents. SETAL A E 41 X can be combined in various ratios with nitrocellulose to formulate wood lacquers. Because of its unusually fast drying rates, SETAAL A E 41 X has gained particular significance in wood lacquers for application on production lines using conveyor dryers.

SETAL 84 XX-70 is a very good durability, excellent colour and gloss retention , high body. It is used: Stoving enamels, car body enamels, enamels for domestic appliances, laboratory equipment, electric apparatus etc. Clear and pigmented acid curing finishes. Clear and pigmented nitrocellulose lacquers. Clear and pigmented polyurethane lacquers. Roller coatings for high stoving temperatures (120-160 °C), especially overprint varnishes. Coil coatings.

Air and forced drying industrial coatings with fast drying and high hardness. Specialty coatings for glass, precious metals and plastics. It is used as air drying coating systems Viacryl SC 200/40X is mainly used for fast drying industrial paints. The dried films are noted for very high hardness and excellent resistance poperties e.g. against water and diluted acids. For air-dried systems (tack-free in 15 minutes) Viacryl SC 200 can be used alone or in combination with plasticizers. Such systems compared with systems using Viacryl SC 200 as sole binder show better pigment wetting and flexibility. The use of plasticizers will, however have a negative influence on alkali resistance. The compatibility of Viacryl SC 200 with other coatings ingredients should be controlled from time to time. Stoving enamels For stoving systems Viacryl SC 200 is generally formulated with plasticizers and urea or melamine resins. The following ratios habe proven successful: Viacryl SC 200 : amino resin : plasticizer = 70 : 15 : 15 or 65 : 15 : 20 (on solids). Compared with air drying systems such systems show after curing (e. g. 30 min/140 °C) improved flexibility, hardness, impact and chip resistance. Specialty coatings For air drying as well as stoving systems Viacryl SC 200 can be used to formulate specialty coatings with good adhesion to glass, precious metals, and various plastics such as ABS and polyphenylene oxide (PPO).