ADDITOL XL 102 is used to improve the effectiveness of paint removers containing paraffine and wax. Post treatment with organic solvents is not necessary.

ROSKYDAL XP 2072 is especially suitable for conventional- or UV-curing (transparent or pigmented) topcoats and pigmented sealers for wood and furniture. properties for applications by spraying or curtain in UV- or conventionalcuringsystems. ROSKYDAL XP 2072 is usually used as the sole binder. If made necessary by the application (high amount) and compatibility exists, it can be flexibilized with other ROSKYDAL grades, e.g. ROSKYDAL 550 or E 70.

SETAL A F 681 TBA is in the formulation of decorative paints with excellent through-drying and good yellowing resistance. Also for flow coatings, DIY paints and air-drying coatings. General SETAL A F 681 TBA is low-viscosity long-oil alkyd resin which is ideal for use in the formulation of DIY and decorative paints with excellent through-drying, a dust-free drying time of approx. 3.5 hours and a tack-free drying time of approx. 6 hours. Because of the relatively high acid value of SETAL A F 681 TBA, the following driers should be used: 0.04 % colbalt 6, 1.20 % zirconium 18 and 0.20 % calcium 4. The metal content is always calculated on the solvent-free resin. The use of these driers ensures good drying stability, even after prolonged storage. The addition of an anti-skinning agent is recommended. Aliphatic hydrocarbons are used to thin SETAL A F 681 TBA. Higher boiling fractions are particularly suitable for adjusting the brushing viscosity. Standard pigments can be used to colour the formulations. The compatibility with alkaline pigments must always be tested in each individual case

SETAL A E 41 X is a short-oil, fatty acid-modified alkyd resin with extremely low viscosity. In the formulation of nitrocellulose lacquers for wood. Nitrocellulose lacquers. SETAL A E 41 X is an alkyd resin with extremely low viscosity for use in the formulation of nitrocellulose lacquers. It is characterized in particular by the following: unusually fast drying rates, especially at high wet film thicknesses, high flexibility and hardness, excellent sandability and high body combined with good sag resistance of the films on wood, excellent lightfastness, excellent intercoat adhesion. The extremely low viscosity of SETAL A E 41 X results in higher solids contents. SETAL A E 41 X can be combined in various ratios with nitrocellulose to formulate wood lacquers. Because of its unusually fast drying rates, SETAAL A E 41 X has gained particular significance in wood lacquers for application on production lines using conveyor dryers.